DESCRIPTION
Phenolic resin, based on Novolak with Hexamine.
Characteristics Unit Specification Test Value
Physical State-Form - - Powder
Melting point °C 75-95 95
Hexamine content % 7,0-7,5 7.3
Flow at 125°C mm 31-34 34
Particle size 75µ % 0-1,6 0.3
Free phenol % 0-1 0.5
|
TUNCA
|
Cure(S)
|
Degree of fluidity(mm)
|
Free phenol (%)
|
Hexa content(%)
|
Finess
|
Characteristic
|
|
Grade
|
150℃
|
(%)
|
|
TRM-RS-1
|
90-130
|
30-45
|
≤1.5
|
7.5-9.5
|
97
|
Pure phenolic resin
|
|
TRM-RS-2
|
70-105
|
≥22
|
≤1.0
|
8.0-10.0
|
97
|
Pure phenolic resin
|
|
TRM-RS-3
|
70-105
|
26-40
|
≤1.0
|
6.5-8.5
|
97
|
Pure phenolic resin
|
|
TRM-RS-4
|
60-90
|
≥25
|
≤1.7
|
8.0-10.0
|
97
|
Cashew modified
|
|
TRM-RS-5
|
60-90
|
30-50
|
≤2.2
|
6.5-8.5
|
97
|
Cashew modified
|
|
TRM-RS-6
|
60-100
|
≥18
|
≤1.5
|
7.5-9.5
|
97
|
Pure phenolic resin
|
|
TRM-RS-7
|
60-90
|
20-35
|
≤2.2
|
6.5-8.5
|
94
|
Rubber modified
|
|
TRM-RS-8
|
50-90
|
≥30
|
≤2.0
|
6.5-8.5
|
97
|
Cashew, boron modified
|
|
TRM-RS-9
|
85-110
|
30-45
|
≤1.5
|
6.5-8.5
|
97
|
Pure phenolic resin
|
|
TRM-RS-10
|
90-120
|
≥30
|
≤2.2
|
6.5-8.5
|
94
|
Rubber modified
|
|
TRM-RS-11
|
80-100
|
≥22
|
≤1.5
|
8.0-10.0
|
97
|
Cashew, melamine, boron modified
|
|
TRM-RS-12
|
80-130
|
20-40
|
≤3.5
|
15.0
|
97
|
|
This product is thermoplastic phenolic resin dried from phenol and formaldehyde. Strong points: high thermal decomposition, good fluidity, low content of free phenol. Mainly used in producing brake pad, brake shoe in the train, brake lining etc